PROPRIEDADES MECÂNICAS E MICROESTRUTURAIS DE JUNTAS SOLDADAS DE AÇO CARBONO PELO PROCESSO HÍBRIDO LASER-GMAW

Abstract

Hybrid Laser-GMAW process, generally known as HLAW (Hybrid Laser Arc Welding), was developed many years ago, but only recently started to be used in industrial applications. In this work, it has been done an evaluation of its process performance when welding a 10mm thick plate of a C-Mn Steel, as well as, the determination of mechanical properties and metallurgical structure of the welded joint, using impact and hardness tests and microstructural characterization. Residual stress was also measured in the plate welded with hybrid process, comparatively to a welded joint performed with GMAW process. The results of performance evaluation of hybrid process showed that it has higher productivity when compared to GMAW. The mechanical properties of the hybrid welded joint were in accordance with base metal requirements.O processo de soldagem híbrido LASER- GMAW, comumente designado por HLAW (Hybrid Laser Arc Welding), foi concebido há bastante tempo, mas só recentemente começou a ser aplicado industrialmente. Nesse trabalho foi feita uma avaliação do seu desempenho na soldagem de chapas de aço C-Mn com 10mm de espessura. As juntas produzidas foram avaliadas por meio de ensaios de impacto Charpy-V e mapeamento de microdureza Vickers, além da caracterização microestrutural. Também foram realizadas, medições dos níveis das tensões residuais introduzidas na junta soldada pelo processo híbrido, comparativamente com o processo GMAW. Os resultados da avaliação de desempenho do processo híbrido mostraram maior produtividade em relação ao GMAW. As propriedades mecânicas da junta soldada mostraram-se compatíveis com os requisitos do material de base.